• Wettability of paint to substrate
    • 2019-08-16 15:12:30
    • admin

    The adhesion of the paint film is caused by the mutual attraction between the paint and the polar groups on the surface of the coated substrate, and the mutual attraction between the polar groups is based on the premise that the paint is well wetted on the surface of the coated substrate.Since the wet condition of the coating on the surface of the coated substrate depends on the surface tension of...

  • Cohesion and thermal expansion coefficient of paint film
    • 2019-08-15 15:14:55
    • admin

    Cohesion and thermal expansion coefficient of paint film The force caused by the cohesion of molecules of the same substance is called cohesion.The more cohesive the coating, the worse the adhesion.In the drying process of paint, with the increase of solvent volatilization and crosslinking degree, the cohesion between film forming material molecules increases, the film produces shrinkage...

  • Polarity of paint film and painted surface
    • 2019-08-06 13:31:41
    • admin

    From the viewpoints of molecular structure, molecular polarity and molecular interaction force, the adhesion of the paint film results from the polar group orientation of the polymer molecules in the coating, and its polar group with the polar molecules on the surface of the coated object. The mutual attraction between each other.Only when the polar phase of the two is adapted to obtain ...

  • Adhesion type and adhesion property of paint film on substrate
    • 2019-08-05 14:25:56
    • admin

    Adhesion type and adhesion property of paint film on substrate The adhesion of the paint film to the substrate is divided into two types: mechanical adhesion and chemical attachment.Mechanical adhesion depends on the properties of the coated sheet (roughness, porosity) and the strength of the formed film; chemical adhesion refers to the mutual attraction of the paint film molecules and the plate m...

  • Some surface properties of plastic substrate affect coating, and coating related properties
    • 2019-08-03 13:28:20
    • admin

    Some surface properties of plastic substrate affect coating, and the properties related to coating mainly include the following aspects: Due to the characteristics of the plastic substrate itself, its smooth and compact, low surface energy is not conducive to the wetting and adhesion of the coating on the substrate. The crystallinity of the plastic affects the adhesion of the film, and its crystal...

  • Characteristics of plastic substrate and its effect on coatings
    • 2019-08-02 13:40:42
    • admin

    Plastics are classified into two types: thermosetting and thermoplastic.Among them, thermosetting plastics have high cross-linking density, good solvent resistance and heat resistance, relatively high surface polarity, and wide range of coatings available.For example, unsaturated polyester is called polyester fiberglass. The texture is hard and polar, and there are many coatings that can...

  • Steel use environment and corrosion conditions
    • 2019-08-01 13:58:02
    • admin

    The steel is subjected to different degrees of corrosion conditions in different operating environments. According to the corrosion conditions, the environmental conditions used by the steel are divided into four grades: Steel use environment and corrosion conditions Steel use environment and corrosion conditions Definition Performance Requirements Coating Effect Harsh conditions Products used in ...

  • Wood coating process
    • 2019-07-30 13:52:02
    • admin

    Wood coating process 1.There are many large holes in the hard wood, putty or hole adding agent to flatten; 2.Apply closing primer after hole filling; 3.If you need to deepen the surface texture of the wood and highlight the wood grain, you can apply the closed primer and apply the water color; 4.After conditioning the wood grain, apply two closed primer; 5.Finish with top coat. Sinograce Chem...

  • Effect of wood substrate on coatings
    • 2019-07-29 11:01:22
    • admin

    Due to the chemical composition of the wood and the particularity of the wood fiber, if it is not handled properly, the water-based paint film will be damaged. Wood is composed of cellulose and a small amount of gum, resin (rosin), pigment, tannin and the like. Although the amount of gum, resin, pigment, tannin, etc. is small, it has a large negative impact on the properties of the coating (mainly...