Common problems with water-based paint: oil slick surface of paint Problem: The finished product has floating black spots or impurities on the surface. A lot of coating produce technical personnel to had encountered similar problem, there is in coating production process "small bubble" or small black dot cannot eliminate. Carefully examine these "little bubbles" ~ they are actually small black oil...
Asked by water-based paint experts: water-based wood lacquer wood grain display is not clear enough Question: Our company is now doing the first coat of wood lacquer and tried a water-based resin (polyurethane). and there is no problem with the adhesion.The current problem is that after adding color essence, it is applied to the floor and the wood grain display is not clear enough. The amount of t...
Common problems with water-based paint: the coating contains bubbles and degassing Phenomenon: During the production of waterborne coating, it is found that the coating contains bubbles after thickening.The bubble volume is big bubble, the volume is small bubble, This kind of phenomenon often happens in paint of equal thickness thick pulp of elastic drawing. Bubble may cause pinhole or prickly hea...
Ask the water-based paint expert -water-based glass paint appears prickly heat when baking Problem: I use water-based acrylic and amino resin to make the glass paint when baking prickly heat. The details are as follows: Temperature: 80 degrees Time: 2 minutes It was already smooth when it was put into the oven Flash dry for 10 minutes Has been changed to defoamer, leveling agent, solvent, no effec...
Leveling and rheological properties of waterborne coatings Problem: water borne white coating wants to have certain rheological already, want to maintain just right leveling sex again, how to do？ Response： This problem is one of the characteristics and technical characteristics of water based paint，In principle, it is mainly the relationship between equilibrium viscosity and rheology (plasticity)....
Water-based wood paint runs off oil---Ask a water paint expert Question: Waterborne wood lacquer should run oil to a rainy day only, or brush one day, also can run oil when waiting for the 2nd day to brush again, did especially ugly later . Water-based white paint does not have this problem. The problem ofwater-based varnish is obvious. Answer： Although it is a water-based paint, the film is hydro...
April 12, 2019, the 40-days orange war ended, every partners in this war to pay 100% of the effort, made a different victories,, although the end of the war, but we never give up, the spirit of teamwork will always be maintained, let us move forward.
Problem：Some of the materials used in the construction of wood products are plywood and wood chip fiberboard. One of the rubber is the most afraid of water, water paint spray will dissolve the inside of the glue. The effect that USES close lacquer also is not ideal, how should solve? Is it easy to use sinograce chemical raw material solution? thank you . Response:This type of wood is usually ...
Common problems of water based paint: causes of shrinkage and solutions Shrinkage, known as cratering, is a common problem with water-based paints。The main cause of shrinkage cavity is impurities in water-based paint. In particular, there is oil in the area where the shrinkage cavity occurs, making the area unable to be wetted.In practical operation, the main causes of shrinkage cavity are as foll...
Question: how to make water-borne heat-resistant paint and water-borne silver powder paint? Whose resin is better? Can you provide the reference formula? Response: Hello, Mr.Zheng,We have received many similar requests for reference formulations.Industrial coatings are characterized by their complexity.It is water borne anti-rust paint likewise,because use environment and the different that ask, f...
Oil pocket phenomenon in water-based paint Problem: To make furniture with transparent colors, in order to save the craft and achieve the purpose of simple construction. We added water-based Color Concentrate to the topcoat for spraying, and the resulting topcoat contained some oil pockets or other unacceptable "face problems." Reply: Aqueous color concentrates are generally made of metal complexe...
Problem：I have not done waterborne polyurethane, the waterborne paint is a rookie .I have never done water - based, water -based is a rookie，I wonder if waterborne polyurethane also needs curing agent? If you want to use it, what is the ratio?Because of the presence of water, is it possible to go back and consume the curing agent?And I want to use this to make the electroplated silver, is it ok? R...
Is the water-based wood paint film as hard as possible? In the market of waterborne wood lacquers, hardness is one of the most concerned indicators for many Chinese waterborne paint developers and users.In the traditional concept, the harder the paint film, the better. There are often customer consultations for ways to get the paint film to 2H or even 3H.Although waterborne wood lacquers have impr...
Filming aids in waterborne coatings Problem : Why do you need to add filming aids to one-component waterborne coatings? The emulsion alone does not form a film. Filming aids are added to form a film. Why does the film-forming auxiliary volatilize, which is still a complete film, and is different from a film without a filming aid? Why can't a single emulsion be fused by water to produce a capillary...
Waterborne two-component paint seeds and loss of light - ask water-based paint experts Question: Hello! I have two problems with the double-surface water-based topcoat. One is that when the film is thick, it is easy to produce rash [related to defoaming agent or related to water and curing agent to produce CO2?]. One is a double component. After mixing for 2 hours, it will lose light. What is the ...
The relationship between film formation and MFFT of waterborne coatings This week, Mr. Li asked us three questions through our questioning water-based paint expert column. This is the second problem: Problem: Film formation above MFFT, no film formation below MFFT, what happens during above or below the MFFT, resulting in film formation? Above MFFT, the emulsion particles are soft and hard below. ...
sinograce chemical
Sinograce Chemical is professional technical enterprise providing solutions of surface materials and manufacturing of raw materials. Sinograce Chemical Company is composed of R&D center, Manufacture center, Quality control department, Market center and International trade department. We have been dedicating to research on excellent paint/coating, adhesive for over 15 years. And now still conti...
Room 1013, Building A5, Financial Port Center, Yangzijiang Road, Baohe District, Hefei City， Anhui province, China
+86 0551 63459511
Copyright © 2015-2025 Anhui Sinograce Chemical Co., Ltd..All Rights Reserved.powered by dyyseo.com
top
English
français
русский
español
العربية