Oil pocket phenomenon in water-based paint Problem: To make furniture with transparent colors, in order to save the craft and achieve the purpose of simple construction. We added water-based Color Concentrate to the topcoat for spraying, and the resulting topcoat contained some oil pockets or other unacceptable "face problems." Reply: Aqueous color concentrates are generally made of metal complexe...
Is the water-based wood paint film as hard as possible? In the market of waterborne wood lacquers, hardness is one of the most concerned indicators for many Chinese waterborne paint developers and users.In the traditional concept, the harder the paint film, the better. There are often customer consultations for ways to get the paint film to 2H or even 3H.Although waterborne wood lacquers have impr...
Filming aids in waterborne coatings Problem : Why do you need to add filming aids to one-component waterborne coatings? The emulsion alone does not form a film. Filming aids are added to form a film. Why does the film-forming auxiliary volatilize, which is still a complete film, and is different from a film without a filming aid? Why can't a single emulsion be fused by water to produce a capillary...
Wood closed primer formula solves the outstanding problem of wood grain Wood bulges and deforms or wood grain protuberant,It is a common problem in wood painting. We discussed the causes and solutions of this problem in this year's topic.In the article on wood grain protrusions - water-based paints, we recommend three technical solutions: 1. Use a saturated coating of 3-4% binder solids....
Factors Affecting Shrinkage of Waterborne Coating Films In practice, the main causes of shrinkage are as follows: 1. The substrate is contaminated by oil or impurities 2. Apply a paint to the old paint or finish without sanding 3. The interval between constructions of the two paints is too long 4. Too much defoamer in the paint The following focuses on two factors: defoamer and impurity contaminat...
Abstract: Reducing the shrinkage of water-based paint film is focused on prevention,designing a rational paint formulation,controlling the paint manufacturing process, and strictly controlling the detection of paint materials, which can reduce the chance of shrinkage. Shrinkage holes have been caused, and it is usually difficult to completely solve them. It is necessary to control the degree of sh...
Basic knowledge of water-based paint In order to provide product development support to a wide range of waterborne coating formulation technicians and waterborne coatings sales personnel, we hav collected and summarized a large number of domestic and international market trends and technical points. Visit our waterborne coatings knowledge base and you can see all of our formulation techniques and ...
Classification and characteristics of waterborne coatings - Waterborne acrylic coatings The emulsifier that USES when polymerization can be anionic, also can be nonionic or cationic, corresponding latex and the lacquer that make also can call anionic, nonionic or cationic. Acrylic waterborne wood lacquer is a variety of applications that have been used earlier and are still in large quantities. Si...
Classification and characteristics of water-based coatings - water-based alkyd paints The vegetable oil is reacted with an acid anhydride after alcoholysis to form an alkyd resin, and the content of the hydrophilic group can be increased to form a water-soluble or water-dispersible resin.Water-soluble water-based alkyds are quite transparent in appearance but have color,The alkyd emulsion was brow...
In the formulation of waterborne wood lacquer topcoats, the binder is a key component in forming the film and determining the properties of the film. The binder, ie the polymer emulsion, dispersion or hybrid, accounts for more than 80%, preferably more than 90%.Since the solid content of the emulsion, especially the aqueous dispersion is relatively low (the aqueous dispersion is generally 30% to 3...
Water - based coating formulation design system - matting agent Matting agents are additives used to control the gloss of waterborne wood coatings to meet the broad needs of mainstream matt paints in today's market.The extinction mechanism of the matting agent can be arranged in an orderly manner on the surface of the coating film, so that the surface of the coating film is uneven, causing the lig...
In the solid paint, white paint is taken as an example. The amount of titanium dioxide should be sufficient to ensure that the paint film has sufficient capping power. The amount of titanium dioxide should not be lower than 13%, but it is not necessary to be higher than 22%. The situation is the same as solvent-based white paint. Fillers may be added or not added. However, a small amount of filler...
Wood coating process 1.There are many large holes in the hard wood, putty or hole adding agent to flatten; 2.Apply closing primer after hole filling； 3.If you need to deepen the surface texture of the wood and highlight the wood grain, you can apply the closed primer and apply the water color； 4.After conditioning the wood grain, apply two closed primer； 5.Finish with top coat. Sinograce Chemical ...
Adhesion type and adhesion property of paint film on substrate The adhesion of the paint film to the substrate is divided into two types: mechanical adhesion and chemical attachment.Mechanical adhesion depends on the properties of the coated sheet (roughness, porosity) and the strength of the formed film; chemical adhesion refers to the mutual attraction of the paint film molecules and the plate m...
Cohesion and thermal expansion coefficient of paint film The force caused by the cohesion of molecules of the same substance is called cohesion.The more cohesive the coating, the worse the adhesion.In the drying process of paint, with the increase of solvent volatilization and crosslinking degree, the cohesion between film forming material molecules increases, the film produces shrinkage phenomeno...
The adhesion of the paint film is caused by the mutual attraction between the paint and the polar groups on the surface of the coated substrate, and the mutual attraction between the polar groups is based on the premise that the paint is well wetted on the surface of the coated substrate.Since the wet condition of the coating on the surface of the coated substrate depends on the surface tension of...
sinograce chemical
Sinograce Chemical is professional technical enterprise providing solutions of surface materials and manufacturing of raw materials. Sinograce Chemical Company is composed of R&D center, Manufacture center, Quality control department, Market center and International trade department. We have been dedicating to research on excellent paint/coating, adhesive for over 15 years. And now still conti...
Room 1013, Building A5, Financial Port Center, Yangzijiang Road, Baohe District, Hefei City， Anhui province, China
+86 0551 63459511
Copyright © 2015-2025 Anhui Sinograce Chemical Co., Ltd..All Rights Reserved.powered by dyyseo.com
top
English
français
русский
español
العربية