Water based polyurethane resin refers to a binary colloidal system in which a polyurethane resin is dissolved or dispersed in water.Water-based polyurethane resin has the advantages of easy to use, stable performance, strong adhesion, excellent gloss, good heat resistance, etc. It can be suitable for various printing methods, especially suitable for screen printing, plastic packaging and composite films. The water-based polyurethane used in the ink industry requires good gloss, high bonding strength to materials, and good blocking resistance at a certain temperature.According to these performance requirements, there are the following requirements for the structural characteristics, functionality, synthetic formula, and process of polyurethane:(1) Select appropriate polyacids and polyols to synthesize polyester polyols with temperature resistance;(2) the introduction of polar groups with strong adhesion to the material;(3) Selecting suitable raw materials to improve the crystallinity of polyurethane;(4) Use coupling agents and other auxiliaries to improve the moisture and heat resistance of water-based polyurethane adhesives for inks. At present, water-based polyurethane inks have been commercialized, can meet a variety of performance requirements, and are receiving increasing attention.The application of water-based polyurethane inks is mainly flexographic printing and gravure printing. Water-based polyurethane inks widely used abroad have good environmental protection, stable ink properties, high viscosity, strong tinting power, and high fastness. need. Sinograce chemical produces polyurethane resin for various polyurethane coatings, such as water-based glue and water-based polyurethane waterproof coating visit us sinograce chemical: https://www.sinogracechem.com Get a Quote Now :sales@sinogracechem.com Telephone               :+86 0551 63459511

Waterborne paint testing and standards:hardness Hardness is one of the most important physical properties of a coating. Coating hardness reflects the coating's ability to resist constant dents, scratches, scribes, and penetrations caused by a hard object. Testing the hardness of materials with different methods will give different results because the testing methods are for different amounts of materials, and each method has its own scale to determine the hardness characteristics of the material. Due to different emphasis, there is no absolute scale that can unify the hardness measured by different methods, but the results obtained by one method are comparable. The commonly used hardness test method for wood coatings is the pencil hardness method. The hardness side measured by pencil hardness test focuses on the coating's resistance to dents, scratches, and scratches. Although some people think that the technical content of pencil hardness is very low, but because it is simple and practical and can be directly measured on wood, the pencil hardness method is still widely used in the coating industry. Before the preparation of the sample, the wood should be polished, smoothed and cleaned. The dry thickness of the coating should be between 25 and 40 μm. It should be dried for 7 days after painting. The film thickness and long drying time affect the hardness test results. The set of pencils used for the test consisted of the hardest 9H to the softest 6B. Commonly used are 4H, 3H, 2H, H, F, HB, B, 2B, 3B, 4B, 5B, and 6B. F is the intermediate hardness, etc., "H," means "Hardness", "B" stands for "Blackness" The hardness of a pencil is determined by the ratio of graphite and clay used in the manufacture of lead cores. The darker, the softer; the more clay, the harder the lead core made. The hardness number of the pencil is used to indicate the hardness of the paint film. Test the pencil first to remove the wooden rod to expose a lead of about 3mm in length. The pencil should be ground vertically on the sandpaper to make a flat surface, and the edges should be sharp. Hold the pencil so that it is 45 degrees from the paint surface to be tested. Corner, apply pressure, and continuously draw the pencil lead on the paint surface. Each hardness pencil is measured 5 times on the sample, each time with a new sharp-lead lead, find the pencil number that scratched or scratched the paint at least 2 out of 5 times, and then use a soft The number one pencil test, if you get no more than one sting or scratch, the latter number is set as the hardness of the coating. In order to eliminate the deviation caused by uneven force and angle of holding the pencil, various pencil hardness testers have been put on the market. The range of pencil hardness grades has a wide range, which cannot reflect the small hardness difference between paint lacquers, that is, the actual soft hardness of paint films with the same pencil hardness may be significantly different. However, the pe...

As a professional manufacturerof label and package printing coating industry, Anhui Sinograce Chemical Co., Ltd took part in this exhibition.he exhibition focused on showing the company's coatings in the field of coatings, including water-based label film adhesive and water-based label paper adhesive,inks,top coating and primers coating ,Other glue,coating additives etc. In the five day of the show, our booth attracted great attention from visitors all over the world. Some of our products in glue, ink and topcoat have become a highlight of this exhibition. Our products are favored by many new and old customers. Many of the participants in the exhibition are very interested in the products of the our products. Many customers are on-site detailed consultation, hoping to take this opportunity to a further cooperation. Through the exhibition, we reached a cooperation agreement or intention with many customers, carried out friendly exchanges and made to many new friends, learned the latest dhesive label Label and inks,top coating and primers coating ,Other glue,coating additives market, opened up an international perspective, which will also bring new opportunities in the future to the development of Sinograce Chemical.

Spraying construction paint film than brush paint film more flat. Spray with water-based wood paint should be added on the basis of the original paint 5% ~ 30% of the tap water dilute after use, for the viscosity of the paint water should also increase, the diluted paint after its coating a 4 cup viscosity should be around 18 ~ 20s. Dilute mix well should be static at least 20 minutes, until the bubbles into the basic disappearance of coating. Before spraying the paint must be more than 200 mesh filter, so as not to bring impurities, affecting the quality of paint film. Water - based paint can be used ordinary spray machine or high - pressure airless spray machine construction. Pay attention to not too fine atomization, but also to prevent bad atomization. The amount of paint should not be too large, not spray too thick, wet film thickness around 50um is good, or easy to produce flow hang, orange peel and other ills. Water-based paint spraying common mistake is a construction too thick, if you want to increase the film thickness, it is appropriate to use multiple spraying method. When spraying on the vertical surface, the spray gun should be slightly at an Angle to the construction surface. Avoid excessive spraying on the vertical surface to avoid sagging. The two paints must be sanded with more than 400# sandpaper. The compressed air is blown off and cleaned with a damp cloth, which increases the adhesion between the two paint films. Sinograce chemical industry co., LTD. Specializes in producing waterborne coatings, waterborne wood lacquer, etc. To learn more, please click here visit us sinograce chemical: https://www.sinogracechem.com Get a Quote Now :sales@sinogracechem.com Telephone :+86 0551 63459511