Formulation design system for waterborne coatings - film forming AIDS The polymer constituting the emulsion or dispersion generally has a glass transition temperature higher than room temperature. In order for the emulsion particles to be well fused into a uniform paint film, it is necessary to reduce the minimum film formation temperature (MFFT) of the crystallization aid.Film forming agents are ...
The film-forming aids for waterborne wood coatings are generally alcohol ether type solvents. The most commonly used filming aids such as diethanol ethers, propylene glycol ethers and N-methylpyrrolidone have high and low boiling points.Water-based wood coatings in the summer construction, the water volatilization is faster, that is, the surface is relatively fast, some of the moisture may be encl...
Defoamer is one of the most difficult additives in waterborne wood coatings to control the balance between defoaming and leveling.The paint liquid will generate bubbles during the application due to agitation .If the bubbles present in the paint are not removed in time, the film will dry and form an unacceptable flaw.The paint also produces air bubbles during production, pumping and filling. Defoa...
Waterborne paint formulation design system - pH regulator Waterborne wood coatings may also need to adjust the pH when necessary.Most emulsions or aqueous dispersions have been adjusted to a pH of 8 to 9 when they are produced, eliminating the need for pH adjusters when making paint.If the pH value is different, add 0.05% to 0.1% of the pH adjuster during the paint making process, and adjust the p...
Adhesion type and adhesion property of paint film on substrate The adhesion of the paint film to the substrate is divided into two types: mechanical adhesion and chemical attachment.Mechanical adhesion depends on the properties of the coated sheet (roughness, porosity) and the strength of the formed film; chemical adhesion refers to the mutual attraction of the paint film molecules and the plate m...
Sinograce Chemical - Jingangtai rafting trip On August 17th, Sinograce Chemical Marketing Center carried out the second quarter group building activities of the Rapids Warriors, blue sky and white clouds, green mountains and green waters, riding a rubber boat, leaping in the cool water, Sometimes light as a swallow, Now and then it gallops like a tiger, the event The thrills not only make the...
Adding certain kinds and dosages of substrate wetting agent and adhesion promoter to the transparent base formulation helps to improve the adhesion of the paint film; the type and quality of the color paste are not only related to the phase of the color paste and the transparent base. Capacity also has a certain influence on the adhesion of the paint film. The thickness of the paint film, the dryi...
1.The tool Before using the soft brush, thoroughly soak it in clean water, remove excess water, and do not drip. The enamel paint should only reach half the length of the bristles.Brush as fast as possible, gently and smoothly brush the wood grain, do not apply it back and forth repeatedly, because the water-based paint is fast drying and the opening time is short, so it should be completed as soo...
3.Process variations of different paint types-Waterborne wood paint application process 2 Applying a matt lacquer to the varnish can change the coating to a matte finish, while applying a varnish to a matt lacquer reduces the brightness of the film and does not achieve maximum brightness and transparency. The color paint of waterborne wood lacquer can be divided into two types: coloured coating an...
Current problems with waterborne polyurethane adhesives: (1) Low solid content: At present, the solid content of water-based polyurethane (WPU) can reach 45%. Fewer systems lead to higher drying and transportation costs. Increasing the solid content leads to an increase in the viscosity of the system, which makes emulsification and dispersion difficult. Reduced emulsion stability. (2) Slow drying ...
Precautions for using two-component polyurethane adhesives 1.Before applying the adhesive, the surface of the adherend must be clean, dry and free of grease. 2.The resin and curing agent should be mixed in the required ratio. 3.When scraping the glue, please try to scrape it carefully as it has a defoaming effect. 4.Store adhesive in (> 10, <50 * C) and dry place 5.Run out of the mixed glue ...
Material property (pu for short) is divided into: Pouring polyurethane elastomer (CPU for short) is one of the most widely used polyurethane elastomers with the largest yield. Thermoplastic polyurethane elastomer (TPU) -- thermoplastic polyurethane elastomer accounts for about 25% of the total amount of polyurethane.Mixed polyurethane elastomer (MPU) - accounts for about 10% of the total amount of...
Glass fiber is an important reinforcing material for the manufacture of fiber reinforced plastics (FRP), and is also used for weaving high temperature resistant fiber cloth.But the glass fiber that has not been treated is brittle, easy to take static electricity after friction, and the surface is smooth, when making the reinforcing material of the resin is not easy to stick with the resin.In the m...
1.The cause of a back adhesion: (1)the paste itself anti-viscosity, especially in the wet weather easy to stick back; (2)After the printing is completed, it is packaged without perfect heat treatment; (3)adjust the slurry formula is not appropriate, adding too much transparent slurry easy to cause back adhesion; (4)transport or storage conditions are not good, in high temperature, high humidity co...
The choice of solvent In the printing ink manufacturing process, in consideration of the overall solvent system of the ink volatility, to improve the printing ink solvent release and reduce the solvent organic solvent residue, the use of solvents are often several volatile mixed solvents.In the printing ink manufacturing process, the main organic solvents are toluene, butanone, cyclohexanone, ethy...
Plasticizer is widely used in industrial production of polymer materials auxiliaries, also known as plasticizers. All substances added to polymer materials that increase polymer plasticity are called plasticizers. The use of plasticizer can improve the properties of polymer materials, reduce production costs and improve production efficiency. is a class of important chem...